Flux-cored wire for NICKEL-BASE ALLOYS | ||||||
CARBO F-Ni CO |
MF23-GF-250-CKNPTZ | C:0,08 Cr: 16 | High temperature resistance alloy for hot working tools. When first applied to | |||
Ni: Rest Mo: 16 | hot forging dies, the overlay is very cohesive. Put under impact, pressure | |||||
220-260 HB | Co: 2,5 V: 0,35 |
load and high temperature, the resulting overlay increases hardness up to | ||||
G, S | workhardened | W:4,5 Fe:< 5 | 400 HB without deforming. The deposit is heat and wear resistant and | |||
ca. 420 HB | resistant to oxidation, reduction and other corrosive media. | |||||
CARBO F-Ni 520 |
MF23-GF-350-CKPTZ | C: 0,05 Cr: 19 | Carbo F- 520 produces a Cr-, Co-, Mo-, Ti-, Al- and W- alloyed nickel base | |||
Ni: Rest Mo: 5 | deposit. The weld metal is a precipitated, easily hardened alloy with an | |||||
330-350 HB | Co: 11 V: 0,3 |
exceptional combination of high temperature mechanical properties, | ||||
G | verfestigt: | W:5 Ti: 3 | formability and corrosion resistance. The alloy can be used for hot forging | |||
35-45 HRC | Al: 1,7 | dies, hot working steels, hot shear blades, etc. | ||||
CARBO F-Ni 625 |
SG-NiCr 21 Mo 9 Nb | C: 0,05 Mn: 0,5 | ||||
Cr: 22 Ni: Rest |
Alloy for a wide range of applications including joining of dissimilar | |||||
ERNiCrMo-3 | Mo: 9 Nb: 3,5 |
steels and repairs on cast iron. | ||||
G | W.-Nr. 2.4831 | Fe: <5,0 | When used for hardfacing, deposit gives up to 350 HB. | |||