Flux-cored wire for ABRASION- and HEAT-RESISTANT APPLICATIONS | ||||||
CARBO F-64 |
MF10-GF-65-GZ | C: 3,8 Cr: 22 | C-, Cr-, B-, W-, V-alloyed flux-cored wire that deposits a very hard | |||
V: 1 W: 2 | martensitic micro structure with carbides. The deposit is resistant against | |||||
O | 62-64 HRC | B: 1 | strong mineral abrasion at higher temperatures. The hardness decreases | |||
about 15% at 400°C, about 25% at 600°C | ||||||
CARBO F-65 |
MF10-GF-65-GZ | C: 5,2 Cr: 21 | High C-, Cr-, Mo-, Nb-, V-, W-alloyed flux-cored self shielding wire which | |||
Mo: 7 Nb: 7 | forms extremly hard carbides. This is used for hard facings against extremly | |||||
O | 63-64 HRC | V: 1 W: 2 | strong mineral wear. The deposit retains it’s wear resistance up to 650°C. | |||
At 400°C the hardness decrease about 4%, at 650°C about 10%. | ||||||
CARBO F-68 |
MF10-GF-70-GCZ | C: 5 Si: 0,8 | Very high C-, Cr-, B-alloyed flux-cored wire electrode for extreme hard and | |||
Cr: 27 V: 7 | non-corrosive hardfacing against high mineral wear also at high tempratures. | |||||
O | 66-68 HRC | The weld deposit has a ledeburitic structure, bearing many various | ||||
hypereutictic carbides. | ||||||
CARBO F-70 |
MF10-GF-65-G | C: 5,2 Si: 1 | High C-, Cr-, V-alloyed flux-cored wire electrode for high abrasive wear. | |||
Cr: 27 V: 7 | The weld deposit consists of crome- and vanadium-carbides. | |||||
O | 62-64 HRC | Weld metal is not machinable. |