X: TOOL STEEL | ||||||
CARBODUR | E 3-UM-60-ST | C: 0,3 Si: 0,5 |
Basic coated electrode for high wear resistant hardfacings on hot- and | |||
WZ 11 B | Mn: 0,9 Cr: 9 |
cold-working tools. The deposit has a crack- free martensitic structure. | ||||
Mo: 1,5 W: 9 |
For achieving optimal crack free deposits preheating of the base material | |||||
=+ | HRC: 57-59 |
to 250°C-300°C is essential. | ||||
CARBODUR | E 3-UM-55-T | C: 0,25 Cr: 3,5 | Particularly suitable for the hard facing of tools and components where | |||
WZ 49 AC | Mo: 1 V: 0,2 |
the carbon content exceeds 0.6%, the full hardness being achieved in | ||||
a single layer without cracking. Deposits give exellent bonding features. | ||||||
=+/~ | Extended service life when post-weld heat treatment is given. | |||||
CARBODUR | E 3 -UM-50-T | C: 0,3 Cr: 2,2 |
High-quality electrode with approx.120% recovery. Used for repairing | |||
WZ 50 AC | W: 4,2 V: 0,6 |
steels of same type, e.g. on hot working tools, and for overlaying edges | ||||
=+/~ | (Material No.:1.2567) | HRC: approx. 47 |
or surfaces of tools made of low alloyed high density steels. | |||
CARBODUR | E 3-UM-55-T | C: 0,4 Si: 0,45 |
For repair and build up of hotworking tools such as slab-shears, hot | |||
WZ 54 AC | Mn: 1,4 Cr: 7,5 |
forging dies, crushing equipment of similar or lower alloyed base metal. | ||||
Mo: 2,5 | The preheat and interphase temperature should be held between 250°C | |||||
=+/~ | HRC: 52-57 |
and 300°C depending on the base metal and it’s heat abduction. | ||||
CARBODUR | E 4-UM-60-ST | C: 0,4 Cr: 4,8 |
AC-weldable electrode with a recovery of 150% for repairing hot | |||
WZ 59 AC | Mo: 3,7 W: 3,5 |
working tools made of steels of same or similar type. The deposited | ||||
weld metal is highly resistant to extreme abrasive wear as well as | ||||||
HRC: 58-60 |
medium shock and impact. The weld metal structure can still be | |||||
=+/~ | improved by subsequent heat treatment. | |||||
CARBODUR | E 4 UM-60-ST | C: 0,9 Cr: 4,5 |
For repair and rebuilding of high speed tool steels. Examples are cutting, | |||
WZ 60 AC | Mo: 8,5 W: 2 |
piercing and shaving tools, hot working punches and dies, extrusion | ||||
V: 1,5 | moulds and dies,shear-blades,milling and cutting tools,swaging hammers, | |||||
=+/~ | (Material No: 1.3346) | HRC: 59-62 |
wood cutting tools and cutting edges on stamping dies. | |||
CARBODUR | E 4-UM-65-ST | C: 0,8 Cr: 4,5 |
AC-weldable electrode with a recovery of 140%. Designed for hard- | |||
WZ 61 AC | Co: 5 W: 18 |
facing high-speed steel tools, low alloyed base materials and for | ||||
V: 1,5 Mo: 1 |
reinforcing cutting edges.The weld metal’s high tungsten content provides | |||||
excellent edge-holding quality. It also has good tempering properties and | ||||||
=+/~ | (Material No: 1.3255) | HRC: 60-63 |
allowes heat treatment like other high speed steels. | |||
CARBODUR | E 4_UM-350_CKPSTZ | C: 0,03 Si: 0,3 |
For the repair of die steels specifically huge volume pressing tools with | |||
WZ 6356 B | Ni: 18 Mo: 4 |
particular reference to H13 and mar aging steels.The deposits are easy | ||||
Co: 12 Ti: + |
machinable and heat treatable where improved hardness is required. | |||||
Facing of dies, stamping tools,metal drawing tools, pressure die, casting | ||||||
HB 350 as welded |
tools. The weld metal deposit gives improved edge hardness to cold | |||||
=+ | HRC:55 soft annealed |
cutting tools and shears. |