XI. NICKEL-BASED ALLOYS | ||||||
CARBOWELD 135 |
EL-NiCr 28 Mo | C: 0,02 Cr: 28 | CARBOWELD 135 was developed to weld materials in conjunction with | |||
(2.4653) | Mo: 3,7 Cu: 1,8 |
low alloyed type steels as well as intermediate and top plating layers. | ||||
Ni: 36 | The deposited overlay leaves a pierce and tension resistant deposit | |||||
that is also resistant to intergranular corrosion, specifically from acids | ||||||
and non oxidizing materials.Operating temperature -196°C up to 350°C | ||||||
=+/~ | YS=350 TS=550 IV=50 at -196°C E=30 | |||||
CARBOWELD 190 |
ENiCu-7 | C:<0,03 Si: 0,4 |
Designated for butt welding and surfacing of nickel-copper, copper- | |||
(2.4366) | Mn: 2 Cu: 31 |
nickel and nickel-copper plated steels. Also recommended for | ||||
EL-NiCu 30 Mn | Fe:<2,5 Al:<0,1 | dissimilar joining like steel/nickel-copper or steel/copper/copper/nickel. | ||||
Ti:<0,5 | CARBOWELD 190 is an alloy with stength and exellent resistance to a | |||||
Ni: rem. | range of media including sea water,dilute hydrofluoric and sulphuric | |||||
acids. Operating temperature -196°C up to 350°C | ||||||
=+/~ | YS=300 TS=500 IV=90(Room Temperatur) IV=50 at -196°C E=>35 | |||||
CARBOWELD A |
ENiCrFe-3 | C: 0,04 Cr: 16 |
Nickel base electrode with a basic coating for joining and cladding | |||
(2.4807) | Mn: 7 Fe: 8 |
stainless-, heat resistant- and cold tenacious steels. Scale-resistant | ||||
EL-NiCr 15 FeMn | Nb: 1,8 Ni: rem. |
up to 1300°C. Operating temperature -196°C up to 550°C | ||||
=+/~ | YS=370 TS=650 IV=82 at -196°C E=35 | |||||
CARBOWELD 82 B |
ENiCrFe-2/MOD | C:<0,04 Cr: 19 | Basic-coated electrode with an alloyed core wire. Suitable for joining | |||
(2.4648) | Mn: 3,5 Fe:<4 | and cladding low alloyed and alloyed steels, welding iron and nickel | ||||
EL-NiCr 19 Nb | Nb: 2 Mo: 1 |
base alloys and for dissimilar joints. Approvals: TÜV | ||||
=+/~ | Ni: rem. | YS=420 TS=700 IV=96 at -196°C | ||||
CARBOWELD 182 |
ENiCrFe-2/MOD | C: 0,04 Cr: 16 |
Nickel base electrode with a recovery of 140% and excellent weldabi- | |||
(2.4620) | Mn: 4 Mo: 1 |
lity on AC, even at low voltages. Suitable for joining and cladding | ||||
EL-NiCr 16 Fe Mn | Fe:<6 Nb: 2 |
stainless, heat resistant and cold tenacious steels as well as welding | ||||
Ni: Rest | dissimilar materials for example low alloyed steels with Ni-base or | |||||
Cu-base alloys.Free of embrittlement at high and low temperatures, | ||||||
=+/~ | non scaling up to 1000°C, and cold tough down to -269°C. | |||||
CARBOLLOY Co |
ENiCrMo-5 | C: 0,06 Cr: 16 |
The CARBOLLOY Co type deposit has outstanding physical | |||
(2.4883) | Mo: 16 Co: 2 |
caracteristics and is resistant to both, oxidating and reduction corrosion | ||||
E 23-UM-250-CKNPTZ | W: 4 Fe: 5 |
It work hardens under impact and machining to ca.400HB-even at high | ||||
=+/~ | Ni: rem. | temperatures- without deforming the deposit. YS=500 TS=680 E=>10 | ||||
CARBOLLOY C 276 B |
ENiCrMo-4 | C:<0,02 Cr: 16 |
CARBOLLOY C 276 B is a lime coated, high alloyed nickel base electrode | |||
(2.4887) | EL-NiMo 15 Cr 15 W | Mo: 16 W: 4,2 |
for welding NiMoCr-alloys such as C 276. The resulting deposit is | |||
E 23-UM-250-CKNPTZ | V: 0,2 Fe: 5 |
resistant to oxidation and reduction corrosion. Overlays are extraordinarily | ||||
Ni: Rest | tough and harden with impact stress and high temperatures to about | |||||
=+ | 400 HB without deforming the deposit. YS= 450 TS=720 E= >30 | |||||
CARBOWELD 625 |
ENiCrMo-3 | C: 0,04 Cr: 22 |
CARBOWELD 625 is a nickel base electrode with a recovery of 140% | |||
(2.4621) | Mo: 9 Fe:<6 | and exellent weldability on AC even at low voltages. Suitable for joining | ||||
EL-NiCr20 Mo 9 Nb | Nb: 3,5 | and cladding stainless, heat resistant and cold tencious steels as well | ||||
Ni: Rest | as welding dissimilar materials for example low alloyed steels with | |||||
Ni-base ore Cu-base alloys. Non-scaling up to 1100°C and cold tough | ||||||
=+/~ | down to -196°C. YS=500 TS=750 IV=40 at -196°C E=35 | |||||
CARBOWELD 625 B |
ENiCrMo-3 | C:<0,03 Cr: 22 | CARBOWELD 625 B is a lime coated nickel base electrode. | |||
(2.4621) | Mo: 9 Fe:<5 | Suitable for joining and cladding stainless, heat resistant and cold tencious | ||||
EL-NiCr20 Mo 9 Nb | Nb: 2,7 | steels as well as welding dissimilar materials for example low alloyed | ||||
Ni: Rest | steels with Ni-base ore Cu-base alloys. Non-scaling up to 1100°C | |||||
= + | and cold tough down to -196°C. YS=500 TS=750 IV=40 at -196°C E=35 |