IV. Electrodes for welding Special Applications | ||||||
CARBO 4009 MPR | E410-17 | C: 0,05 Mn: 0,6 | Rutile coated electrode with a recovery of 160% for plating | |||
E 13 R 52 | Cr: 13 | and joining equal and similar ferrit Cr-steels and cast steels. | ||||
=+/~ | HB:190 | YS=420 TS=680 E=18 | ||||
CARBO 4015 MPR | E430-16 | C: 0,11 Mn: 0,7 |
Rutile coated electrode with a recovery of 160% for corrosion- | |||
E 17 R 52 | Cr: 17 | and wear-proof plating on water, steam and gas valves, | ||||
=+/~ | especially for sulphuric gases. | |||||
CARBO 4115 MPR | EZ17Mo R 52 | C: 0,2 Mn:0,5 | Rutile coated electrode with a recovery of 160% for corrosion- | |||
Cr: 16 Mo: 1,2 | and wear-proof plating on water, steam and gas valves. | |||||
Hardness: as welded HB: 200 after heat treatment: approx. 38 HRC | ||||||
=+/~ | YS=500 TS=700 E=15 | |||||
CARBO 4120 MPR | EZ 13 1 R 52 | C: 0,2 Cr: 14 |
Rutile coated electrode with a recovery of 160% for operating | |||
Mo: 1,2 Ni: 1,0 |
temperature up to 500°C. Scale resistant up to 800°C | |||||
Hardness: as welded HB: 200 after heat treatment: approx. 38 HRC | ||||||
=+/~ | YS=540 TS=730 E=12 | |||||
CARBO 4351 MPR | E410NiMo-16 | C: 0,06 Si: 0,7 |
Rutile coated electrode with a recovery of 150% with a cavitation | |||
E 13 4 R 53 | Mn: 0,6 Cr: 13 |
and erosion resistant weld deposit. | ||||
Ni: 4,5 Mo: 0,5 |
Applications: Bridge stores, deposition to thick areas of water, | |||||
=+/~ | steam and gas fittings YS=700 TS=1100 IV=>43 E=15 | |||||
CARBO 4462 AC |
E2209-17 | C:<0,03 Cr: 22,5 |
Electrode suitable for welding on compound steels of same or | |||
E 22 9 3 N LR 12 | Ni: 9,0 Mo: 3,0 |
similar types. The weld deposit is resistant to pitting, stress corrosion | ||||
N: 0,10 | cracking and intercrystalline corrosion at temperatures up to 250°C. | |||||
=+/~ | YS=610 TS=780 IV=44 at -40°C E=26 Approvals: TÜV, UDT | |||||
CARBO 4462 Cu B |
E 25 9 3 Cu N L B 22 | C: 0,03 Si: 0,8 |
Basic electrode suitable for welding on compound steels of same or | |||
Mn: 0,7 Cr: 25 |
similar type. The weld deposit is resistant to pitting, stress corrosion | |||||
DIN 8555: | Ni: 9 Mo: 4,0 |
cracking and intercrystalline corrosion at temperatures up to 250°C | ||||
E9-um-300-CKR | N: 0,2 Cu: 2,5 |
The deposit gives better corrosion results than the Cu free version. | ||||
=+/~ | YS=700 TS=850 IV=>32 E=30 | |||||
CARBO 4440 AC |
E317L-17 | C:<0,03 Si: 0,8 |
Electrode suitable for joining corrosion-resistant CrNiMoN steels as | |||
E 18 16 5 N L R 12 | Mn: 1,0 Cr: 18 |
well as for austenitic-ferritic joints. The weld metal is very high | ||||
Ni: 17,5 Mo: 4,5 |
corrosion resistant, especially under non oxidizing, halogenious | |||||
N: 0,12 | conditions.The high molbdenum content results in extended resistance | |||||
against pitting intercrystalline corrosion (wet corrosion up to 350°C) | ||||||
=+/~ | YS=400 TS=580 IV=55 at -120°C E=25 | |||||
CARBO 4519 HE |
E385-17/MOD | C: 0,02 Cr: 20 |
Rutile coated electrode with a recovery of 160% well suited for joint | |||
E20 25 5 Cu N L R 53 | Ni: 25 Mo: 4,5 |
welding on the same or similar corrosion resistant CrNiMoCu steels. | ||||
Cu: 1,5 | Overlays leave a pierce and tension resistant deposit. | |||||
=+/~ | YS=380 TS=580 IV=80 at -40°C E=40 Operating temperatur: up to 350°C | |||||
CARBO 4850 B |
EZ 22 33 Nb B 22 | C: 0,15 Si: 0,6 |
Basic coated electrode for joint welding corrosion- and heat-resistant | |||
(Alloy 800) | Mn: 1,6 Cr: 21 |
high alloyed steels and caststeels. The deposit is heat-proof up | ||||
Ni: 33 Nb: 1,2 |
to 1050°C and resistant to carborising, oxidising and reducing gases. | |||||
=+ | YS=380 TS=600 IV=45 E=25 | |||||
CARBO 4853 B |
EZ 25 35 Nb B 22 | C: 0,40 Si: 1,0 |
Basic coated electrode for joint welding corrosion- and heat-resistant | |||
Mn: 2,0 Cr: 24,5 |
high alloyed steels and caststeels.The deposit is heat-proof up | |||||
Nb: 1,3 Ni: 35 |
to 1050°C and resistant to carborising, oxidising and reducing gases. | |||||
=+ | Scale resistant up to 1050°C. | |||||
CARBO 4948 B |
E308H-15 | C: 0,05 Si: 0,5 |
Basic-coated electrode, suitable for welding of austenic CrNi steels | |||
EZ 19 9 B 22 | Mn: 1,5 Cr: 18,5 |
and steel castings with carbon contents higher than 0,4% as well | ||||
Ni: 9,5 | as ACI conform castings. The alloy is high temperatur resistant | |||||
up to 700°C and scale resistant up to 800°C. | ||||||
=+ | YS=450 TS=660 IV=60 E=28 | |||||
CARBO 4846 B |
E310H-15 | C: 0,40 Mn: 2,4 |
High alloyed electrode for centrifugally cast tubes of material HK-40. | |||
E 25 20 H B 22 | Cr: 25,5 Ni: 21,5 |
Used in industrial heating equipment up to 1100°C and for | ||||
petrochemical applications. | ||||||
=+ | Good resistance against fissuring, hot cracking and carburisation. |