VI. COBALT based Electrodes for HARD SURFACING and CLADDING. | ||||||
CARBO S 1 | ECoCr-C | C: 2,2 Si: 1,2 |
AC-weldable hardfacing electrode with an alloyed core and a recovery | |||
Mn: 1,0 Cr: 30 |
of 160%. The deposit is a cobalt base alloy of austenitic-ledeburitic | |||||
E 20-UM-55-CSTZ | W: 12,5 Fe: 3 |
structure with embedded CrW carbides. It is the hardest of the standard | ||||
Co: rem. | cobalt base alloys. The weld metal is highly resistant to corrosion, impact, | |||||
HRC: approx. 55 |
abrasiv wear as well as thermal shocks and heavy mechanical impact. | |||||
=+/~ | Wear pads,rotary seal rings,pump sleeves,centre less grinder work rests | |||||
CARBO SK 6 | ECoCr-A | C: 1,0 Si: 0,9 |
AC-weldable hardfacing electrode with a rutile-basic coating and an | |||
CARBO S 6 | Mn: 1,0 Cr: 28 |
alloyed core. The deposit is a cobalt base alloy of austenitic-ledeburitic | ||||
(S 6 has a recovery | E 20-UM-40-CTZ | W: 4,5 Fe: 3 |
structure with embedded CrW carbides. The weld metal is highly resistant | |||
of 160%) | Co: rem. | to corrosion, impact,abrasiv wear as well as thermal shocks and heavy | ||||
HRC: approx. 42 |
mechanical impact. Good aptitude for polishing and machining. Used on | |||||
=+/~ | steam valves, hot shear blades, hot pressing dies, etc | |||||
CARBO S 12 | ECoCr-B | C: 1,4 Si: 0,9 |
AC-weldable hardfacing electrode with an alloyed core and a recovery | |||
Mn: 1,0 Cr: 28 |
of 160%. The weld metal is highly resistant to corrosion, impact, abrasiv | |||||
E 20-UM-50-CTZ | W: 8,5 Fe: 3 |
wear as well as thermal shocks and heavy mechanical impact. | ||||
Co: rem. | Hardfacing of cutting edges, long knifes and other tools used in the | |||||
=+/~ | HRC: approx. 48 |
wood, plastic, paper, carpet and chemical industry. | ||||
CARBO SK 21 | C: 0,3 Si: 0,9 |
CARBO SK 21 is a rutile-coated electrode which is AC weldable. The | ||||
CARBO S 21 | E20-UM-300-CKTZ | Mn: 1,0 Cr: 28 |
deposit is a cobalt base alloy of high tenacity as well extrem corrosion- | |||
(S21 has a recovery | Mo: 5,5 Ni: 3 |
and heat-resistance. The weld metal is highly resistant to impact and is | ||||
of 160%) | Fe: 3 | work-hardening up to 45 HRC. SK 21 is particularly recommended for | ||||
Co: rem. | use on all work pieces which are subjected to corrosion, impact wear as | |||||
=+/~ | HRC: approx. 30 |
well as high temperatures or termal shocks | ||||
CARBO TS 1 | RCoCr-C | Bare cobalt base rod for oxy-acetylen and TIC-welding . | ||||
WSG 20-GO-55-CSTZ | Applications and alloy see description of CARBO S1 | |||||
HRC: approx. 55 |
||||||
CARBO TS 6 | RCoCr-A | Bare cobalt base rod for oxy-acetylen and TIC-welding . | ||||
WSG 20-GO-40-CTZ | Applications and alloy see description of CARBO S6 / SK6 | |||||
HRC: approx. 42 |
||||||
CARBO TS 12 | RCoCr-B | Bare cobalt base rod for oxy-acetylen and TIC-welding . | ||||
WSG 20-GO-50-CTZ | Applications and alloy see description of CARBO S12 | |||||
HRC: approx. 48 |
||||||
CARBO TS 21 | Bare cobalt base rod for oxy-acetylen and TIC-welding . | |||||
WSG-20-GO-300-CKTZ | Applications and alloy see description of CARBO S21 / SK21 | |||||
HRC: approx. 30 |