CARBO MoB |
E7018-A1 | C: 0,07 Si: 0,6 | Basic-coated Mo alloyed electrode for welding piping-, boiler- and fine grain | |||
E Mo B 42 | Mn: 0,9 Mo: 0,5 | structural steels. Non-ageing weld metal, tough also at low temperature. | ||||
Hot-crack proof and suitable for service temperature up to 550°C. | ||||||
=+ | YS=490 TS=600 IV=>47 at -20°C IV=>120 at Rt. E=25 Approvals: TÜV, DB, CE | |||||
CROMOWELD MoAC | E7013-G | C: 0,07 Si: 0,8 | Rutile-coated Mo alloyed electrode for welding pipe and boiler steels as well | |||
E Mo R 12 | Mn: 0,9 Mo: 0,5 | as fine grain structural steels.The weld metal is non-ageing and tough also | ||||
at low temperatures, hot-crack proof and suitable for service temperature | ||||||
=+/~ | up to 550°C. YS=490 TS=600 IV=>47 E=25 Approvals: TÜV | |||||
CARBO CrMo 1 B | E8018-B2 | C: 0,07 Si: 0,7 | Basic coated CrMo alloyed electrode for welding high-strength joints on low | |||
E CrMo1 B12 H5 | Mn: 0,9 Cr: 1,1 | alloy tempered steels of up to 880 N/mm².Suitable for welding creep-resistant | ||||
Mo: 0,5 | CrMo steels in boiler and piping system construction. Resistant to high | |||||
temperatures up to 500°C. Non-ageing welding deposit, resistant to alkaline | ||||||
solutions, heat-treatable and case-hardenable. Approvals: TÜV, DB, CE | ||||||
=+ | Annealed 30 min. at 720°C YS=500 TS=640 IV=90 E=24 | |||||
CRABO CrMo 2 B | E9018-B3 | C: 0,05 Si: 0,6 | Basic coated CrMo alloyed electrode for welding high-strength joints on low | |||
E CrMo 2 B12 H5 | Mn: 1,0 Cr: 2,3 | alloy tempered steels of up to 1100 N/mm².Suitable for welding creep-resistant | ||||
Mo: 1,0 | CrMo steels in boiler and piping system construction. Resistant to high | |||||
temperatures up to 500°C. Non-ageing welding deposit, resistant to alkaline | ||||||
solutions, heat-treatable and case-hardenable. | ||||||
=+ | Annealed 30 min. at 760°C YS=510 TS=650 IV=80 E=22 | |||||
CARBO CrMo 5 B | E 8018-B6 | C: 0,06 Si: 0,5 | Basic coated CrMo alloyed electrode for welding joints with good mechanical | |||
E CrMo 5 B42 H5 | Mn: 1,0 Cr: 5,1 | properties to low alloyed quenched and subsequently tempered steels | ||||
Mo: 0,5 | up to 1275 N/mm².Suitable for welding heat treatablem, quenched and | |||||
subsequently tempered steels as well as for tubes, resistance to caustic | ||||||
embrittlement for working temperatures up to 600°C. | ||||||
=+ | YS= 490 TS=620 IV=>70 E=>17 | |||||
CARBO CrMo 9 B | E 8018-B8 | C: 0,07 Si: 0,3 | Basic coated CrMo alloyed electrode for welding joints with good mechanical | |||
E CrMo 9 B42 H5 | Mn: 0,7 Cr: 9,0 | properties to low alloyed quenched and subsequently tempered steels. | ||||
Mo: 1,0 Ni: 0,2 | Suitable for welding heat treatablem, quenched and | |||||
subsequently tempered steels as well as for tubes, resistance to caustic | ||||||
embrittlement for working temperatures up to 600°C. | ||||||
=+ | YS= 610 TS=730 IV=>70 E=>19 | |||||
CARBO CrMo 91 B | E 9015-B9 | C: 0,1 Si: 0,35 | Basic coated electrode with low hydrogen content for welding high temperature | |||
E CrMo 91 B42 H5 | Mn: 0,8 Cr: 9,0 | martensitic,creep resistant 9-12 % chromium steels such as P91 and T91. | ||||
Mo: 1,0 Ni: 0,7 | The deposits have good toughness properties even under long term stresses | |||||
V: 0,2 Nb: 0,05 | and high creep rupture strength. | |||||
N: 0,04 | For working temperatures up to 650°C. | |||||
=+ | YS= 650 TS=760 IV=>70 E=>17 |